test

mul-files

  • 1_2moreCyc.mul (Sputtering: E = 1 keV, p(Ar) = 5e-05 mbar, t = 20 min; Annealing: T = 800 K, p(O2) = 1e-07 mbar, t = 20 min)
  • 1_2moreCyc.mul

    Image ID 1_2moreCyc_1
    Datetime 2021-03-12 13:03:29
    Itun 0.23 nA
    Utun 221.9 mV
    Scan Size 100 × 100 nm²
    Resolution 512 × 512
    Tilt
    Scan Duration 77.32 s
    Line Time 151.02 ms
    Offset 0, 0
    Gain 955
    Mode 0
    Sputtering
    Energy1 eV
    p(Ar)5e-05 mbar
    Time20 min

    Annealing
    Temperature800 K
    p(O2)1e-07 mbar
    Time20 min

    SurfacePt(111)
    TipW(etched)
    NAP Gas
    p(NAP) mbar
    Remark

    sputtering: annealing:

    Image ID 1_2moreCyc_2
    Datetime 2021-03-12 13:09:24
    Itun 0.43 nA
    Utun 292.7 mV
    Scan Size 100 × 100 nm²
    Resolution 512 × 512
    Tilt
    Scan Duration 82.82 s
    Line Time 161.76 ms
    Offset 282, 6367
    Gain 955
    Mode 0
    SurfacePt(111)
    TipW(etched)
    NAP Gas
    p(NAP) mbar
    Remark

    nan

    Image ID 1_2moreCyc_3
    Datetime 2021-03-12 13:13:03
    Itun 0.91 nA
    Utun 292.7 mV
    Scan Size 100 × 100 nm²
    Resolution 512 × 512
    Tilt
    Scan Duration 123.12 s
    Line Time 240.47 ms
    Offset -743, 8038
    Gain 955
    Mode 0
    SurfacePt(111)
    TipW(etched)
    NAP Gas
    p(NAP) mbar
    Remark

    nan

    Image ID 1_2moreCyc_4
    Datetime 2021-03-12 13:16:51
    Itun 0.65 nA
    Utun 292.7 mV
    Scan Size 100 × 100 nm²
    Resolution 512 × 512
    Tilt
    Scan Duration 129.34 s
    Line Time 252.62 ms
    Offset -6732, 5803
    Gain 955
    Mode 0
    SurfacePt(111)
    TipW(etched)
    NAP Gas
    p(NAP) mbar
    Remark

    nan

    ID a
    Datetime 2021-05-09 11:51:34
    Surface nan
    slide num 5
    Labjournal Table DAta
    Labjournal Table DAta
    slide num 5
    Remark

    nan

    ID PNG1
    Datetime 2021-05-09 11:51:34
    Surface nan
    slide num 6
    Labjournal Table DAta
    Labjournal Table DAta
    slide num 6
    Remark

    nan